Depth Profiling of Complex Samples Using Confocal Raman Microscopy

Article

Application Notebook

Application NotebookApplication Notebook-02-01-2014
Volume 0
Issue 0

Raman microscopy has evolved into a common method for fast and nondestructive analysis of microscopic samples in forensic and R&D laboratories as well as for troubleshooting in the field of quality control.

Raman microscopy has evolved into a common method for fast and nondestructive analysis of microscopic samples in forensic and R&D laboratories as well as for troubleshooting in the field of quality control. Samples ranging from art and archeology, materials science, biology, pharmacology to polymers and plastics can be investigated. The analysis is performed by scanning a laser beam laterally across the sample resulting in a very high spatial resolution down to less than a micron.

In addition, optically transparent samples can be studied in the z-direction. Therefore confocal Raman microscopy is an extremely useful technique, because it allows nondestructive sample investigation in the third dimension yielding subsurface information without the need of sample preparation such as a microtome cut. By moving the laser focus in z-direction either a complete 2D or even 3D depth profile of a structured sample like a polymer laminate can be generated or in the easiest case an inclusion or contamination inside the matrix of a sample can be identified. In this study two different application examples are given to demonstrate the usefulness of confocal Raman depth profiling.

Instrumentation

The confocal Raman microscope SENTERRA (Figure 1) was equipped with three excitation lasers (532 nm, 633 nm, 785 nm) and a computer controlled xyz stage allowing increment stepping down to 0.1 μm in all directions. The confocal design of the SENTERRA Raman microscope minimizes out-of-focus contributions from unwanted spectral information by optical sectioning in the z-direction utilizing confocal pinholes.

Figure 1: SENTERRA Raman microscope.

The FlexFocus™ design of the SENTERRA allows fast switching between high throughput and confocal modes without the need of realignment of pinholes and slits. Due to the true confocal mode the SENTERRA provides a depth resolution of better than 1 μm.

Figure 2: Conventional vs. confocal microscopy.

Figure 2 shows the principal difference between a conventional and confocal optics. The depth axis is projected onto the y-axis of the detector (Figure 2a) and receives light from a very broad range of different sample planes; in fact the measured spectrum will be an average spectrum of the layer between points Z1 and Z2.

Figure 3: Visual image of the particle inside the syringe.

A confocal optical design can be used to reduce the sampling volume and improve the spatial resolution in order to better discriminate potential spectral differences between Z1 and Z2. The principle of confocal optical microscopy is shown in Figure 2b. In this configuration, a confocal aperture is placed in a remote image plane to reduce the sampling depth of field. In this simple example, the aperture blocks the resultant Raman light scattered from Z2 thus resulting in a spectrum exclusively from Z1. Only the in-focus and on-axis Raman light rays are recorded by the spectrograph system as the out-of-focus and off-axis light rays are blocked by the confocal aperture. The result is that confocal Raman microscopes restrict the sampling depth to a region smaller than for conventional optics. In addition, confocal measurements can also improve the rejection of stray light and reduce fluorescence interference.

Figure 4: From top: Raman spectra of the syringe material, the gel content and the contamination particle.

Application Example: Identification of a Contamination (Particle) Inside a Liquid Filled Syringe

The first example shows the analysis of a particle trapped inside of a gel filled syringe. With standard techniques, it is not possible to analyze such a particle without extensive sample preparation. Normally one would have to isolate, wash, and dry the particle in order to perform a reliable spectroscopic analysis. With the confocal Raman microscope, it is possible to analyze such a particle directly inside the syringe without any sample preparation. Spectra of the syringe material and the gel content were collected separately. Figure 3 shows a visual image of the particle which is about 100 μm in diameter. The resultant spectra of the analysis are shown in Figure 4. The upper red spectrum was measured directly on the surface of the syringe and can be assigned to the polymer material of the syringe tube. The spectrum of the gel content is shown in the middle of Figure 4; obviously the gel consists mostly of water (broad peak around 3300 cm-1, small peak above 1600 cm-1) and an additional organic component (small peak around 2900 cm-1). Finally the spectrum of the contamination can be seen at the bottom of Figure 4; a library search identifies the particle as polypropylene with a good hit-quality of 855 points (max = 1000). Due to distinct spectral differences between the spectrum of the particle and that of the syringe-material, it seems unlikely that the contamination is a fragment of the syringe, and most probably it has an external origin.

Figure 5: 2D depth profiling-plot.

Application Example: Analysis of a Polymer-Laminate

In the second example, the analysis of a thin multicomponent polymer-laminate is shown. For a detailed examination of the laminate, a depth profile was recorded with the SENTERRA Raman-microscope over a range of 68 μm with a step increment of 1 μm. For optimal performance a 100× immersion oil objective was used in combination with a 785 nm laser. The result of the measurement is shown in Figure 5 in a 2D plot. Especially when examining the fingerprint region the laminar structure of the polymer foil becomes evident by the changes in the spectral patterns along the z-axis. Representative spectra of all the layers are shown in Figure 6, and all the layers could be identified by using the library search feature of the spectroscopy software OPUS. With the library search results the laminate structure can be reconstructed as shown on the right side of Figure 6: The sample consists of five layers and three different materials. The outer layers are polypropylene with a thickness of about 20 μm. Both outer layers border on thin polyamide layers which are about 3 and 4 μm in thickness, respectively. The inner layer consists of ethylene vinyl alcohol copolymer (EVOH) with a layer thickness of about 20 μm.

Figure 6: Result of the depth profiling with spectra and reconstructed model of the multilayer structure.

Summary

The SENTERRA Raman microscope is a powerful tool for the evaluation of complex samples and multilayer structures. Due to the confocal design of the SENTERRA it is not only possible to gather high resolution surface information but also to analyze the sample along its z-axis. It is even possible to analyze a sample behind a thick transparent polymer or glass layer, for instance, in a vial or a syringe without the need for any sample preparation. With the OPUS search function and extensive libraries unknown samples can be readily identified.