The thermal treatment of a grafted Sn-SiO

catalyst was monitored in situ using diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). Structural changes and organic intermediates could be observed.

Thermal treatment is an important but oftentimes poorly understood step during the synthesis of heterogeneous catalysts. In situ spectroscopic techniques can provide valuable insights into structural changes of such materials upon heating. 

DRIFTS is an ideal technique for such an application because powder samples can be used without further preparation, high temperatures and pressures can be applied, and gases can be flown over the catalysts easily. 

The FT-IR spectra were recorded by averaging 32 scans with a resolution of 8 cm

. Using the heated environmental chamber inserted into the DiffusIR diffuse reflection sampling accessory (PIKE Technologies), the environmental chamber was flushed with synthetic air at a flow rate of ca. 20 mL/min and heated at a rate of 20 °C/min up to a temperature of 550 °C. Prior to the thermal treatment, the Sn(NMe

 using a grafting technique under static vacuum. 

By applying the environmental chamber and heating the sample up to 550 °C, conditions comparable to the ones in conventional calcination ovens could be achieved. Figure 1 shows spectra recorded at different temperatures. 

 Figure 1: Spectra recorded at 25 Â°C (black), 100 Â°C (light blue), 200 Â°C (purple), 300 Â°C (dark blue), 400 Â°C (red), 500 Â°C (green), and 550 Â°C (yellow).			

At room temperature intense bands between 2750 and 3000 cm

  can be observed which can be assigned to C-H stretch vibrations of the organic Sn precursor. Already at 100 °C these bands significantly decreased, while bands at 3286 cm

  has been assigned to N-H stretch vibrations of ammonium species that could be formed as intermediates on the silica surface upon heating. The other band at 3656 cm

 originates from Sn-OH groups that have been formed due to restructuring of the Sn surface species during the calcination (1). 

  is clearly visible. This band stems from the Si-OH stretch band of isolated silanols (2). The intensity of this band increases upon further heating, indicating the opening of siloxane bridges on the silica surface. 

At 400 °C the intensities of the C-H stretch vibrations have further decreased and the vibration at 3286 cm

  completely disappeared while the Si-OH and Sn-OH stretch bands were still increasing in intensity. At the final temperature of 550 °C, all organic groups have been burned off and the desired and catalytically active Sn sites are present.			

The DiffusIR accessory is a valuable tool to understand structural changes in heterogeneous catalysts during thermal treatment. The sequence of formation of intermediates, Sn-OH and Si-OH, species could be observed. The gained insights can potentially be used to improve the synthesis of catalysts. 

Infrared and Raman Spectroscopy; Principles and Spectral Interpretation

 (Elsevier Inc., San Diego, California, 2011). 

(2)  F. Rascón, R. Wischert, and C. Copéret, 

			6125 Cottonwood Drive, Madison, WI 53719			

Articles

The thermal treatment of a grafted Sn-SiO2 catalyst was monitored in situ using diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS).